A series of Mn-substituted BaMgF(4) samples have been synthesized by a hydrothermal route. X-ray diffraction study reveals that the products are monophasic in nature. Scanning electron microscopy (SEM) and energy-dispersive spectrometry (EDS) studies were carried out to investigate the morphology and stoichiometry for these compounds. X-ray photoelectron spectroscoy (XPS) and electron spin resonance (ESR) studies were done to confirm the oxidation state of dopant ion. Room temperature ferromagnetism was observed on Mn substitution at the Mg site in BaMgF(4) samples. The saturation magnetization increases initially, shows a peaking effect, and then decreases with further increase in Mn concentration in BaMg(1-x)Mn(x)F(4) (0.0 ≤ x ≤ 0.15). However, ferroelectricity was found to decrease with an increase in Mn concentration in the series of investigated BaMg(1-x)Mn(x)F(4) (0.0 ≤ x ≤ 0.15) samples. First-principle calculations, using the projector augmented wave potentials on Mn-substituted BaMgF(4), confirmed the decrease in magnetic moment with an increase in Mn content beyond certain concentration. These samples exhibit very weak magnetocapacitive coupling, which can be attributed to the very small magnetic signal observed in these samples.