Complex oxides--containing at least two different cations on crystallographically distinct sites--have recently been shown to display redox cycling of platinum group metals (PGMs), such as Pd; for example, Pd-substituted complex oxides can reversibly extrude metallic Pd under reducing conditions and then reincorporate Pd(2+) ions into the lattice under oxidizing conditions. The title compounds, YMn(0.5)Fe(0.5-x)Pd(x)O(3-δ) (0 ≤ x ≤ 0.07) crystallizing in the noncentrosymmetric YMnO(3) structure, were prepared using a sol-gel process at 800 °C, and the structures were refined from high-resolution synchrotron X-ray powder diffraction data. Their redox cycling behavior was monitored using synchrotron X-ray diffraction and EXAFS studies. In contrast to the previously studied complex oxide host compounds, YMn(0.5)Fe(0.5-x)Pd(x)O(3-δ) is only modestly tolerant to cycling: repeated redox cycling leads to the formation of PdO, which, on the time-scale of the oxidation cycles, does not reincorporate in the complex oxide lattice. Both oxidized and reduced samples were tested for the oxidation of CO to CO(2) under CO-lean conditions. YMn(0.5)Fe(0.5-x)Pd(x)O(3-δ) performs essentially as well as previously studied YFe(1-x)Pd(x)O(3-δ). The CO oxidation light-off characteristics of the hexagonal hosts are very similar to finely dispersed PdO. Despite evidence that Pd is almost fully dispersed as divalent ions in the host lattice, which is presumably accompanied by the concurrent creation of oxygen vacancies (2 Pd(2+):1 V(O(2-))), the as-prepared hexagonal materials do not display any significant improvement in catalytic activity as a function of Pd substitution level. This suggests that the corner-connected trigonal bipyramids that characterize this structural family do not enable the transport of oxygen through the bulk of the lattice. The study casts light on factors in the solid-state chemistry of precious metal-substituted complex oxides that influence the efficacy of redox cycling of the precious metal, and catalytic performance.