The electrochemistry of anthraquinone-2,6-disulfonate (2,6-AQDS) at glassy carbon (GC), hydrogenated glassy carbon (HGC), the basal plane of highly oriented pyrolytic graphite (HOPG), and boron-doped diamond was investigated by cyclic voltammetry and chronocoulometry. Quantitative determination of the surface coverage and qualitative assessment of the physisorption strength of 2,6-AQDS adsorption on each of these electrodes were done. The diamond and HGC surfaces are nonpolar and relatively oxygen-free, with the surface carbon atoms terminated by hydrogen. The polar 2,6-AQDS does not adsorb on these surfaces, and the electrolysis proceeds by a diffusion-controlled reaction. Conversely, the GC and HOPG surfaces are polar, with the exposed defect sites terminated by carbon-oxygen functionalities. 2,6-AQDS strongly physisorbs on both of these surfaces at near monolayer or greater coverages, such that the electrolysis proceeds through a surface-confined state. Less than 40% of the initial surface coverage can be removed by rinsing and solution replacement, reflective of strong physisorption. The results show the important role of the surface carbon-oxygen functionalities in promoting strong dipole-dipole and ion-dipole interactions with polar and ionic molecules such as 2,6-AQDS. The results also support the theory that diamond electrodes may be less subject to fouling by polar adsorbates, as compared to GC, leading to improved response stability in electroanalytical measurements. The relationship between the 2,6-AQDS surface coverage, the double-layer capacitance, and the heterogeneous electron-transfer rate constant for Fe(CN)(6)(3)(-)(/4)(-) for these four carbon electrodes is presented.