The rapid development of micro- and nanostructures containing silver nanoparticles is based on their unique physical properties. Despite the new applications of silver nanoparticles in nanomedicine are under heavy discussions, silver nanoparticles could be used in liquid radiation detectors thanks to the irradiation-induced surface plasmon resonance (SPR) phenomena observed in the colloidal solutions. Silver nitrate (1 mM AgNO(3)) and sodium citrate (1 wt% and 5 wt% C(6)H(5)O(7)Na(3)) were used as precursors for the fabrication of colloidal solutions. Prepared solutions were exposed to gamma-rays from a (60)Co gamma therapy unit 'Rokus-M' to varying absorbed doses, from 2 to 250 Gy. A UV/VIS/NIR spectrometer (Avantes-2048) was used for the measurement of the optical properties (absorbance) of the silver solutions. It was found that an initial absorbed dose of 2 Gy induced the formation of spherical silver nanoparticles as it was indicated in the absorbance spectrum of the solution, which had a well-pronounced absorption maximum at the wavelength of 410 nm. There is a potential to measure absorbed doses down to around 20 mGy. The SPR peaks at the wavelengths of 500-700 nm were found at the highest investigated doses >100 Gy, indicating the presence of silver nanorods. The colour of colloidal solutions ranged from pale yellow to green and was dependent on the absorbed dose. The investigation has shown that density, size and shape of synthesised silver nanoparticles are dependent on the absorbed dose and that shape transformations of the particles due to irradiation are possible. Application of colloidal solutions containing silver nanoparticles for dosimetric purposes is discussed on the basis of the obtained results.