Phosphanotriylbenzenecarboxylic acid (ptbcH(3); P(C(6)H(4)-p-CO(2)H)(3)) and its methyl phosphonium iodide derivative (mptbcH(3)I; {H(3)CP(C(6)H(4)-p-CO(2)H)(3)}I) have been used as organic building blocks in reaction with Zn(ii) salts to obtain a series of related two-dimensional coordination polymers with honeycomb-like networks. The variable coordination number and oxidation states available to phosphorus have been exploited to produce a family of related phosphine coordination materials (PCMs) using a single ligand precursor. The phosphine carboxylate trianion, ptbc(3-), reacted with Zn(ii) to form 3,3-connected undulating hexagonal sheets based on tetrahedral P and Zn nodes, where Zn-ptbc = 1 : 1. When hydroxide was used as an additional framework ligand, Zn(4)(OH)(2) clusters were obtained. The clusters support 6,3-connected bilayers that consist of pairs of fused hexagonal sheets (Zn-ptbc = 2 : 1) with intra-layer pore spaces. The Zn(4)(OH)(2) clusters are also coordinated by solvent, which was preferentially displaced when the bilayer material was synthesized in the presence of ethylene diamine. Treatment of ptbc(3-) with MeI resulted in methylation of the phosphine to give the P(v) phosphonium iodide salt derivative. The formally dianionic methylphosphonium tricarboxylate building block, mptbc(2-), has the same trigonal-pyramidal bridging geometry as the parent phosphine. However, mptbc(2-) reacted with Zn(ii) on a 1 : 1 stoichiometric ratio to give an unusual trilayer sheet polymer that is based exclusively on 3-connected nodes. Solid-state (31)P NMR studies confirmed that the phosphine ligands were resistant to oxidation upon solvothermal reaction under aerobic conditions.