Uniform multi-walled carbon nanotubes (MWCNTs) were obtained decomposing toluene inside of fused silica tubing previously covered with Co oxide thin film. The two-step process, ruled successively in the same aerosol assisted chemical vapor deposition (AACVD) set up, constitutes a simplified route to the synthesis of MWCNTs. First, Co oxide thin film was deposited inside of fused silica tubing at 723 K, using a precursor solution of Co acetate in absolute methanol. After Co oxide deposition, the covered tubing was heated up to 1173 K under Ar flow, then a mist of toluene was injected inside the tubing, using also Ar as carrier gas, consequently MWCNTs were obtained in the internal wall of the tubing. The Co oxide film and the MWCNTs were analyzed by scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM) and atomic force microscopy (AFM). Uniform and very long MWCNTs (several tens of microm) with diameters around 20 to 100 nm were observed, with the advantage that the content of Co particles inside the nanotube was very low.