Molecular dynamics simulations were used to study the wetting of polymer surfaces with water. Contact angles of water droplets on crystalline and two amorphous polyethylene (PE) and poly(vinyl chloride) (PVC) surfaces were extracted from atomistic simulations. Crystalline surfaces were produced by duplicating the unit cell of an experimental crystal structure, and amorphous surfaces by pressing the bulk polymer step by step at elevated temperature between two repulsive grid surfaces to a target density. Different-sized water droplets on the crystalline PE surface revealed a slightly positive line tension on the order of 10(-12)-10(-11) N, whereas droplets on crystalline PVC did not yield a definite line tension. Microscopic contact angles produced by the simple point charge (SPC) water model were mostly a few degrees smaller than those produced by the extended SPC model, which, as the model with lowest bulk energy, presents an upper boundary for contact angles. The macroscopic contact angle for the SPC model was 94 degrees on crystalline PVC and 113 degrees on crystalline PE. Amorphicity of the surface increased the water contact angle on PE but decreased it on PVC, for both water models. If the simulated contact angles on crystalline and amorphous surfaces are combined in proportion to the crystallinity of the polymer in question, simulated values in relatively good agreement with measured values are obtained.