We demonstrated in this paper the shape-controlled synthesis of hematite (alpha-Fe(2)O(3)) nanostructures with a gradient in the diameters (from less than 20 nm to larger than 300 nm) and surface areas (from 5.9 to 52.3 m(2)/g) through an improved synthetic strategy by adopting a high concentration of inorganic salts and high temperature in the synthesis systems to influence the final products of hematite nanostructures. The benefits of the present work also stem from the first report on the <20-nm-diameter and porous hematite nanorods, as well as a new facile strategy to the less-than-20-nm nanorods, because the less-than-20-nm diameter size meets the vital size domain for magnetization properties in hematite. Note that the porous and nonporous hematite one-dimensional nanostructures with diameter gradients give us the first opportunity to investigate the Morin temperature evolution of nanorod diameter and porosity. Evidently, the magnetic properties for nanorods exhibit differences compared with those for the spherical particle counterparts. Hematite nanorods are strongly dependent on their diameter size and porosity, where the magnetization is not sensitive to the size evolution from submicron particles to the 60-90 nm nanorods, while the magnetic properties change significantly in the case of <20 nm. In other words, for the magnetic properties of nanorods, in a comparable size range, the porous existence could also influence the magnetic behavior. Moreover, applications in formaldehyde (HCHO) gas sensors and lithium batteries for the hematite nanostructures with the diameter/surface area gradient reveal that the performance of electrochemical and gas-sensor properties strongly depends on the diameter size and Brunauer-Emmett-Teller (BET) surface areas, which is consistent with the crystalline point of view. Thus, this work not only provides the first example of the fabrication of hematite nanostructure sensors for detecting HCHO gas, but also reveals that the surface area or diameter size of hematite nanorods can also influence the lithium intercalation performances. These results give us a guideline for the study of the size-dependent properties for functional materials as well as further applications for magnetic materials, lithium-ion batteries, and gas sensors.