The oxygen incorporation reaction in undoped SrTiO(3) was investigated by electrical measurements (pressure modulation technique) in the temperature range from 650-920 degrees C and by means of tracer exchange experiments in the temperature range from 458-600 degrees C. The surface of the undoped SrTiO(3) single crystals was modified by alkaline earth metal compounds leading to a tremendous enhancement of the effective surface exchange rate for oxygen incorporation as compared to the uncoated surface.