Liquid chromatography under limiting conditions of desorption (LC LCD) is a method which allows molar mass independent elution of various synthetic polymers. A narrow, slowly moving zone of small molecules, which promotes full adsorption of one kind of polymer species within column (an adsorli) acts as an impermeable barrier for the fast moving macromolecules. The latter accumulate on the barrier edge and elute nearly in total volume of liquid within column. At the same time, transport of less adsorptive macromolecules is not hampered so that these are eluted in the size exclusion (SEC) mode. As result, polymers differing in their polarity and adsorptivity can be easily separated without molar mass interference. Three methods of barrier creation are discussed and compared. It is shown that a fraction of sample may elute unretained if the adsorli sample solvent is used as a barrier in connection with a narrow-pore column packing. One part of excluded macromolecules likely breaks-out from the adsorli zone and this results in partial loss of sample and distortion of the LC LCD peaks. This problem can be avoided if the adsorli zone is injected immediately before sample solution. Applicability of the LC LCD method for polymer separation has been demonstrated with a model mixture of poly(methyl methacrylate) (adsorbing polymer) and polystyrene (non adsorbing polymer) using bare silica gel as a column packing with a combination of tetrahydrofuran (a desorption promoting liquid -a desorli) and toluene (adsorli). It has been shown that the LC LCD procedure with tandem injection allows simple and fast discrimination of polymer blend components with good repeatability and high sample recovery. For quantitative determination of molar masses of both LC LCD and SEC eluted polymers, an additional size exclusion chromatographic column can be applied either in a conventional way or in combination with a multi-angle light scattering detector. A single eluent is used in the latter column, which separates the mixed mobile phase, system peaks and the desorli zone from the polymer peaks so that measurements are free from disturbances caused by the changing eluent composition. The resulting LC LCD x SEC procedure has been successfully applied to poly(methyl methacrylate) samples.