A study of the electrostatic enhancement of collection efficiency of filters pretreated with ionic surfactants has been carried out in controlled conditions with monodisperse aerosols. Cationic surfactant (dimethyl dioctadecylammonium bromide [DDAB]) and anionic surfactant (sodium oleate [SO]) were used to pretreat polypropylene fibrous filters as the positively and negatively charged filters, respectively. The effects of aerosol size, aerosol charge state, face velocity, aerosol type, and relative humidity (RH) were considered to elucidate their influence on the aerosol penetration. Results indicate that penetration through surfactant-pretreated filters was lower than that through untreated filters, and pretreatment of the filter with surfactant was observed not to affect the structure of the filter. The electrofieldmeter direct-measured the very clear electric field of filter when treating ionic surfactants. The results proved that pretreatment with surfactant caused filters to become charged. Comparing penetration through surfactant-pretreated filters with that through untreated filters with neutral aerosol, the penetration reduction factor of the surfactant-pretreated filters was in the range 1.3-2.2. Comparing aerosol penetration through the surfactant-pretreated filters with singly charged aerosol with that through untreated filters with uncharged aerosol indicates that the former decreases by a factor of 1.8-48.8. The surface fiber charges of the DDAB- and SO-pretreated filters were calculated to be 2.02 x 1(-10) C/m and -1.53 x 10(-1) degrees C/m. Moreover, the aerosol penetrations through the surfactant-pretreated filters increased with the face velocity. Surfactant-pretreated filters performed better against solid aerosol than against liquid aerosol. RH has no effect on aerosol penetration through the surfactant-pretreated filters. Regression equations for Coulombic and dielectrophoretic single-fiber efficiencies in terms of the dimensionless parameters could be fitted by the experimental measurements of surfactant-pretreated filters in this work.