Helical poly(3-methyl-4-vinylpyridine) (P3M4VP)/amino acid complexes have been prepared via acid-base reaction of the achiral polymer with D and L amino acids: alanine, leucine, valine, serine and phenylalanine. The circular dichroism (CD) spectra of P3M4VP/D- and L-alanine complexes in CH(3)OH/H(2)O show opposing (near mirror image) Cotton effect signals at 278.4, 274.8 and 270.8 nm, indicating the formation of enantiomeric secondary structures. The formation of the enantiomeric structures is supported by observed [alpha](D)(25) values of -3.0 and +3.0 for the P3M4VP/D-alanine and P3M4VP/L-alanine complexes, respectively. The preparation of helical P3M4VP/amino acid complexes has been carried out in CH(3)OH and H(2)O at pH 1.8 and 2.7. The intensities of the Cotton effect signals were good. For example, for the P3M4VP/L-alanine complexes in CH(3)OH/H(2)O and H(2)O (pH 1.8), the second Cotton effect signal around 275-277 nm show [theta;] values of 49 980 and 79 210 deg . cm(2) . dmol(-1), respectively. The formation of the helical secondary structure is rapid. The acid-base reaction between P3M4VP and L-alanine in CH(3)OH/H(2)O, in 10 min, show a CD spectrum with Cotton effect signals at 274 and 272 nm with [theta] values of 27,000 deg . cm(2) . dmol(-1) and -36,000 deg . cm(2) . dmol(-1), respectively. P3M4VP permits ready conformational reorientation on complexation with amino acids, but once the helical P3M4VP/amino acid complexes are formed, it is stable at room temperature. P3M4VP is not compatible with HeLa ovarian cancer cells, but the helical P3M4VP/amino acid complexes are compatible with HeLa cells. The complexes minimally interfere with the adhesion and growth of HeLa cells on complex surfaces. Helical poly(3-methyl-4-vinylpyridine)/D- and L-alanine complexes support the attachment and growth of HeLa cells. The micrographs shows HeLa cells after three days: left panel: on P3M4VP/L-alanine complex; right panel: on P3M4VP/D-alanine complex.