The dynamic structure factor of vitreous silica and glycerol has been measured as a function of temperature and of the momentum transfer up to Q=0.105 nm(-1) using a novel experimental technique, the inelastic ultraviolet scattering. As in the case of Brillouin light scattering and ultrasonic measurements, the temperature dependence of the acoustic attenuation shows a plateau below the glass transition whose amplitude scales as Q2. Moreover, a slight temperature dependence of attenuation has been found in vitreous silica at about 130 K, which seems to be reminiscent of the peak measured at lower Qs. These two findings strongly support the idea that anharmonicity is responsible for sound attenuation at ultrasonic and hypersonic frequencies. Finally, we demonstrate that the attenuation mechanism should show a change of regime between 0.105 and 1 nm(-1).